| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃×5N | ASTM D-1238 | 2.2 | g/10min |
| 熔体流动速率 | 220℃×100N | ASTM D-1238 | 30 | g/10min | |
| 物理性能 | 比重 | ASTM D-792 | 1.09 | ||
| 全光线透过率 | 2mm | ASTM D-1003 | 90 | % | |
| 成型收缩率 | 2mm | 0.4-0.6 | % | ||
| 雾度 | 2mm | ASTM D-1003 | 1.8 | % | |
| 燃烧性 | UL 94 | 1.5mmHB | |||
| 机械性能 | IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 155 | J/m |
| 弯曲弹性模量 | ASTM D-790 | 2100 | MPa | ||
| 弯曲强度 | ASTM D-790 | 68 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 50 | M | ||
| 拉伸强度 | ASTM D-638 | 40 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 111 | R | ||
| 热性能 | 维卡软化点 | 50N | ASTM D-1525 | 90 | ℃ |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D-648 | 83 | ℃ | |
| 热变形温度 | 12.7mm,1.82MPa | ASTM D-648 | 87 | ℃ | |