| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 40 | g/10min | |
| 密度 | ASTM D-1505 | 0.905 | g/cm3 | ||
| 熔化温度 | TOTAL Method | 160-165 | ℃ | ||
| 机械性能 | 屈服拉伸强度 | ASTM D-638 | 25 | MPa | |
| 伸长率 | ASTM D-638 | 6 | % | ||
| 弯曲模量 | ASTM D-790 | 1170 | MPa | ||
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 100 | J/m | |
| IZOD缺口冲击强度 | -20℃ | ASTM D-256 | 44 | J/m | |
| Charpy冲击强度 | 23℃ | DIN 53453 | 8 | kJ/m2 | |
| Charpy冲击强度 | -20℃ | DIN 53453 | 5 | kJ/m2 | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 148 | ℃ | |
| 热变形温度 | ASTM D-648 | 95 | ℃ | ||