产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.07 | ||
| 邵氏硬度 | ASTM D2240 | 70 | |||
| 熔流率 | 200℃/10kg | ASTM D1238 | 32 | g/10min | |
| 黄度指数 | E313 | ＜15 | |||
| 耐磨性 | ASTM D3489 | 7 | mg | ||
| 成型收缩率 | 流向 | ASTM D955 | 0.008 | mm/mm | |
| 错流方向 | ASTM D955 | 0.008 | mm/mm | ||
| 机械性能 | 抗张强度 | ASTM D412 | 25.5 | MPa | |
| 拉伸应力 | 100% | ASTM D412 | 3.4 | MPa | |
| 300% | ASTM D412 | 5.2 | MPa | ||
| 断裂伸长率 | ASTM D412 | 770 | % | ||
| 撕裂强度 | ASTM D624 | 60.5 | kN/m | ||
| 弯曲模量 | 23℃ | ASTM D790 | 18.6 | MPa | |
| 压缩永久变形 | 22hrs,70℃ | ASTM D395B | 30 | % | |
| 22hrs,23℃ | ASTM D395B | 11 | % | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 75 | ℃ | |