产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.955 | g/cm3 | ||
| 熔体流动速率 | MI | 190℃/2.16kg | ASTM D-1238 | 0.35 | g/10min | |
| HLMI | 190℃/21.6kg | ASTM D-1238 | 33 | g/10min | ||
| 机械性能 | 屈服拉伸强度 | 50mm/min | ASTM D-638 | 27 | MPa | |
| 肖氏硬度 | ASTM D-2240 | 63 | ||||
| 正切弯曲模量 | ASTM D-790 | 1370 | MPa | |||
| 断裂伸长率 | 50mm/min | ASTM D-638 | >600 | % | ||
| 耐环境应力开裂性 | 条件A,F50100% lgepal | ASTM D-1693 | 45 | h | ||
| 耐环境应力开裂性 | 条件B,F50100% lgepal | ASTM D-1693 | 35 | h | ||
| 热性能 | 脆化温度 | ASTM D-746 | <-75 | ℃ | ||