| 厂家(产地) | 韩国韩华 |
|---|---|
| 牌号 | 2030 |
| 加工级别 | 注塑级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 0.8 | g/10min | ||
| 密度 | ASTM D-1505 | 0.929 | g/cc | |||
| 机械性能 | 断裂拉伸强度 | ASTM D-638 | 190 | kg/cm2 | ||
| 断裂伸长率 | ASTM D-638 | 740 | % | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 260 | kg/cm2 | ||
| TD | ASTM D-882 | 240 | kg/cm2 | |||
| 断裂伸长率 | MD | ASTM D-882 | 350 | % | ||
| TD | ASTM D-882 | 650 | % | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 83 | ℃ | ||
| 熔点 | ASTM D-2117 | 101 | ℃ | |||
| 其它性能 | 拉伸抗热强度 | MD | ASTM D-1004 | 85 | kg/cm | |
| TD | ASTM D-1004 | 90 | kg/cm | |||
| 醋酸乙烯含量 | HCC | 6.5 | Wt% | |||
| 混浊度 | ASTM D-1009 | 4.0 | % | |||
| 厚度 | HCC | 0.06 | mm | |||
| 下降冲击强度 | ASTM D-1709 | ＞400 | g | |||