| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 机械性能 | 断裂伸长率 | 23℃ | ASTM D-638 | 2.6 | % |
| 拉伸模量 | 23℃ | ASTM D-638 | 10000 | MPa | |
| 挠曲模量 | 23℃ | ASTM D-790 | 8965 | MPa | |
| 埃佐缺口冲击强度(lzod) | 23℃ | ASTM D-256 | 112 | J/m | |
| 埃佐无缺口冲击强度(lzod) | 23℃ | ASTM D-4812 | 998 | J/m | |
| 挠曲强度 | 23℃ | ASTM D-790 | 200 | MPa | |
| 拉伸强度 | 23℃ | ASTM D-638 | 140 | MPa | |
| 电气性能 | 表面电阻率 | --- | ASTM D-257 | 0.1E15 | Ohm |
| 耗电因数 | 1E3Hz/1E6Hz | ASTM D-150 | 0.002/0.018 | --- | |
| 介电常数 | 1E3Hz/1E6Hz | ASTM D-150 | 4/3.8 | --- | |
| 介电强度(短时) | 1.6mm/3.2mm | ASTM D-149 | 23/17 | Kv/mm | |
| 体积电阻率 | --- | ASTM D-257 | 1E16 | Ohm-cm | |
| 加工性能 | 干燥时间，除湿式干燥机 | --- | --- | 2-4 | h |
| 干燥温度 | --- | --- | 110-130 | ℃ | |
| 加工湿度率 | --- | --- | ＜0.04 | % | |
| 熔胶温度 | --- | --- | 240-260 | ℃ | |
| 模温 | --- | --- | 30-130 | ℃ | |
| 热性能 | 熔融点 | --- | ASTM D-3418 | 225 | ℃ |
| 热变形温度 | 0.45MPa/1.8MPa | ASTM D-648 | 220/205 | ℃ | |
| 其它性能 | 比重 | --- | ASTM D-792 | 1.53 | --- |
| 收缩率 | 纵向/横向 | --- | 0.3/1 | % | |
PBT
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(PTA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。