| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.948 | g/cm3 | |
| 熔体流动速率 | MI21.6 | ASTM D-1238 | 0.05 | g/10min | |
| 机械性能 | 拉伸降伏强度 | ASTM D-638 | 240 | kg/cm2 | |
| 艾氏缺口冲击强度 | ASTM D-256 | >30 | kg·cm/cm | ||
| ESCR | ASTM D-1693 | >1000 | Hours | ||
| 拉力断裂伸长率 | ASTM D-638 | 850 | % | ||
| 硬度 | ASTM D-2240 | 64 | Shore D | ||
| 抗拉冲击强度 | ASTM D-1822 | 750 | kg/cm2 | ||
| 拉伸断裂强度 | ASTM D-638 | 360 | kg/cm2 | ||
| 热性能 | 脆化温度 | ASTM D-746 | ＜-70 | ℃ | |
| 熔点 | FPC方法 | 129 | ℃ | ||
| 软化点 | ASTM D-1525 | 122 | ℃ | ||