| Property | Test Condition | Unit | Standard | guide value |
| | d.a.m. | cond. |
| Rheological properties |
| C | Molding shrinkage, parallel | 60x60x2; 270 °C / WZ 80 °C; 600 bar | % | ISO 294-4 | 1.1 | |
| C | Molding shrinkage, transverse | 60x60x2; 270 °C / WZ 80 °C; 600 bar | % | ISO 294-4 | 1.1 | |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | |
Mechanical properties (23 °C/50 % r. h.) |
| C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 3800 | 1500 |
| C | Yield stress | 50 mm/min | MPa | ISO 527-1,-2 | 85 | 50 |
| C | Yield strain | 50 mm/min | % | ISO 527-1,-2 | 4.1 | >20 |
| C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 60 | N |
| C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 50 | 80 |
| C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
| Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 55 | N |
| Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 55 | 60 |
| Izod notched impact strength | | kJ/m² | ISO 180-1A | <10 | <10 |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 3700 | 1600 |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 125 | 55 |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 5.8 | 7,8 |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 120 | 40 |
Thermal properties |
| C | Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 265 | |
| C | Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 80 | |
| C | Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 212 | |
| Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 230 | |
| C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.8 | |
| C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.7 | |
| | | | | | |
| C | Oxygen index | Method A | % | ISO 4589-2 | 34 | |
| Glow wire test (GWFI) | 0.4 mm | °C | IEC 60695-2-12 | 960 | |
| Glow wire test (GWIT) | 0.4 mm | °C | IEC 60695-2-13 | 775 | |
Electrical properties (23 °C/50 % r. h.) |
| C | Relative permittivity | 100 Hz | - | IEC 60250 | 4.0 | 8.0 |
| C | Relative permittivity | 1 MHz | - | IEC 60250 | 4.0 | 4.0 |
| C | Dissipation factor | 100 Hz | 10-4 | IEC 60250 | 120 | 2000 |
| C | Dissipation factor | 1 MHz | 10-4 | IEC 60250 | 190 | 550 |
| C | Volume resistivity | | Ohm·m | IEC 60093 | 1E12 | 1E11 |
| C | Surface resistivity | | Ohm | IEC 60093 | 1E15 | 1E13 |
| C | Electric strength | 1 mm | kV/mm | IEC 60243-1 | 30 | 25 |
| C | Comparative tracking index CTI | Solution A | V | IEC 60112 | 600 | |
Other properties (23 °C) |
| C | Density | | kg/m³ | ISO 1183 | 1169 | |
Processing conditions for test specimens |
| C | Injection molding-Melt temperature | | °C | ISO 294 | 260 | |
| C | Injection molding-Mold temperature | | °C | ISO 294 | 80 | |
Processing recommendations |
| Drying temperature dry air dryer | | °C | - | 80 | |
| Drying time dry air dryer | | h | - | 2-6 | |
| Residual moisture content | | % | Acc. to Karl Fischer | 0.03-0.07 | |
| Melt temperature (Tmin - Tmax) | | °C | - | 260-270 | |
| Mold temperature | | °C | - | 80-100 |