| TYPICAL PROPERTIES (1) |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 550 | kgf/cm? | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 830 | kgf/cm? | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 20000 | kgf/cm? | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 115 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 72 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1870 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 81 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, notched, 0°C | 70 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, notched, -30°C | 65 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 54 | kJ/m? | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 52 | kJ/m? | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 44 | kJ/m? | ISO 180/1A |
| Charpy 0°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m? | ISO 179/1eA |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m? | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 40 | kJ/m? | ISO 179/1eA |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m? | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 110 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 90 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.1E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 155 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 120 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 79 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Specific Volume | 0.83 | cm?/g | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.8 - 1 | % | SABIC Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.8 - 1 | % | SABIC Method |
| Density | 1.19 | g/cm? | ISO 1183 |
| Melt Flow Rate, 250°C/5.0 kg | 13 | g/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 6 | cm?/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 12 | cm?/10 min | ISO 1133 |