| 牌号 | TX1000 |
|---|---|
| 销售方式 | 品牌经销 |
| 用途级别 | 瓶盖专用料 |
| 厂家(产地) | 伊士曼化学 |
| 加工级别 | 注塑级 |
| 特性级别 | 抗化学性,耐高温 |
应用/用途
Appliances
电器
Consumer and durable goods
消费和耐用品
Housewares
家居用品
Small appliances
小家电
Key Attributes
关键属性
Ease of processing
易于加工
Excellent clarity
清晰
Excellent hydrolytic stability
优异的水解稳定性
Fast drying times
快速干燥时间
Good chemical resistance
良好的耐化学性
Good heat resistance
耐热性好
Outstanding impact resistance
出色的抗冲击性
Quick cycle times
快速的周期时间
| Product Data Sheet Eastman Tritan™ Copolyester TX1000 | ||||||||
| ||||||||
| Typical Properties (Preliminary) | ||||||||
| Propertya | Testb Method | Typical Value, Unitsc | ||||||
| General Properties | ||||||||
| Specific Gravity | D 792 | 1.18 | ||||||
| Mold Shrinkage | D 955 | 0.005-0.007 mm/mm (0.005-0.007 in./in.) | ||||||
| Mechanical Properties | ||||||||
| Tensile Stress @ Yield | D 638 | 43 MPa (6200 psi) | ||||||
| Tensile Stress @ Break | D 638 | 53 MPa (7700 psi) | ||||||
| Elongation @ Yield | D 638 | 6% | ||||||
| Elongation @ Break | D 638 | 210% | ||||||
| Tensile Modulus | D 638 | 1550 MPa (2.25 x 105psi ) | ||||||
| Flexural Modulus | D 790 | 1550 MPa (2.25 x 105psi ) | ||||||
| Flexural Yield Strength | D 790 | 62 MPa (9000 psi) | ||||||
| Rockwell Hardness, R Scale | D 785 | 112 | ||||||
| Izod Impact Strength, Notched @ 23°C (73°F) | D 256 | 980 J/m (18.4 ft·lbf/in.) | ||||||
| Impact Strength, Unnotched @ 23°C (73°F) | D 4812 | NB | ||||||
| Mechanical Properties (ISO Method) | ||||||||
| Tensile Strength @ Yield | ISO 527 | 47 MPa | ||||||
| Tensile Stress @ Break | ISO 527 | 58 MPa | ||||||
| Elongation @ Yield | ISO 527 | 7% | ||||||
| Elongation @ Break | ISO 527 | 185% | ||||||
| Tensile Modulus | ISO 527 | 1548 MPa | ||||||
| Flexural Modulus | ISO 178 | 1495 MPa | ||||||
| Flexural Strength | ISO 178 | 59 MPa | ||||||
| Izod Impact Strength, Notched | ||||||||
| ISO 180 | 20 kJ/m2 | ||||||
| ISO 180 | 93 kJ/m2 | ||||||
| Thermal Properties | ||||||||
| Deflection Temperature | ||||||||
| D 648 | 99°C (210°F) | ||||||
| D 648 | 85°C (185°F) | ||||||
| Optical Properties | ||||||||
| Total Transmittance | D 1003 | 90% | ||||||
| Haze | D 1003 | <1% | ||||||
| Typical Processing Conditions | ||||||||
| Drying Temperature | 88°C (190°F) | |||||||
| Drying Time | 4-6 hrs | |||||||
| Processing Melt Temperature | 260-282°C (500-540°F) | |||||||
| Mold Temperature | 38-66°C (100-150°F) | |||||||