| 厂家(产地) | 台湾奇美 |
|---|---|
| 牌号 | CM205 |
| 加工级别 | 注塑级 |
| 特性级别 | 高刚性,高强度,抗紫外线,高光泽 |
| 用途级别 | 照明灯具 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 硬度 | ASTM D-785 | M-95 | ||
| 假密度 | ASTM D-1182 | 0.77 | g/cm3 | ||
| 吸水率 | ASTM D-570 | 0.3 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.19 | ||
| 全光透过率 | ASTM D-1003 | 92 | % | ||
| 流动系数 | ASTM D-1238 | 1.8 | g/10min | ||
| 燃烧率 | 1/16"HB | UL-94 | |||
| 成型收缩率 | ASTM D-955 | 0.002-0.006 | mm/mm | ||
| 机械性能 | 抗冲击力 | ASTM D-256 | 2.0 | kg-cm/cm | |
| 引张强度 | ASTM D-638/PSI | 10200/720 | Kg/cm2 | ||
| 弯曲强度 | ASTM D-790/PSI | 15600/1100 | Kg/cm2 | ||
| 延伸率 | ASTM D-638 | 5.0 | % | ||
| 曲折率 | ASTM D-542 | 1.491 | |||
| 绝缘耐力 | ASTM D-149 | 500 | Volts/Mil | ||
| 抗冲击力 | ASTM D-256 | 0.37 | ft-lbs/in2 | ||
| 电气性能 | 体积固有抵抗 | ASTM D-257 | 1015 | Ω.m | |
| 失电率 | ASTM D-150 | 0.19 | |||
| 诱电率 | ASTM D-150-647b | 3.7 | |||
| 诱电率力 | ASTM D-150-647 | 0.5 | |||
| 热性能 | 热变形温度 | ASTM D-648 | 100/212 | °C/°F | |
| 维卡软化点 | ASTM D-648 | 113/235 | °C/°F | ||
PMMA塑料(有机玻璃)(聚甲基丙烯酸甲脂)英文名称:Polymethyl Methacrylate
比重:1.18克/立方厘米 成型收缩率:0.5-0.7%
成型温度：160-230℃
干燥条件：70-90℃ 4小时
物理性能：透明性极好,强度较高,有一定的耐热耐寒性,耐腐蚀,绝缘性良好,综合性能超过聚苯乙烯,但质脆,易熔于有机溶剂,如作透光材料,其表面硬度 稍低,容易擦花.适于制作透明绝缘零件和强度一般的零件.
成型性能：1.无定形料,吸湿大,需干燥,不易分解,流动性中等,易发生填充不良,粘模,收缩,熔接痕等. 2.宜高压注射,在不出现缺陷的条件下取高料温,高 模温,以增加流动性,降**,改善透明性及强度.模具浇注系统表面应光洁,脱模斜度大,顶出均匀.同时设排气口,以防出现起泡。
应用范围:
汽车工业（信号灯设备、仪表盘等），医药行业（储血容器等），工业应用（影碟、灯光散射器)，日用消费品（饮料杯、文具等）。
注塑模工艺条件:
干燥处理：PMMA具有吸湿性因此加工前的干燥处理是必须的。建议干燥条件为90C、2~4小时。
熔化温度：240~270C。模具温度：35~70C。 注射速度：中等
化学和物理特性:
PMMA具有优良的光学特性及耐气侯变化特性。白光的穿透性高达92%。PMMA制品具有很低的双折射，特别适合制作影碟等。
PMMA具有室温蠕变特性。随着负荷加大、时间增长，可导致应力开裂现象。PMMA具有较好的抗冲击特性。