| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D792 | 1.41 | g/cm3; | |
| 熔体质量流动速率 | ASTM D1238 | 27 | g/10 min | ||
| 成型收缩率 | flow,3.00MM | ASTM D955 | 2.0 | % | |
| 吸水率 | Equilibrium,23℃,60%rh | ASTM D570 | 0.22 | % | |
| 洛氏硬度 | M-Scale | ASTM D785 | 80 | ||
| 机械性能 | 拉伸强度 | Yield,23℃ | ASTM D638 | 62.0 | MPa |
| 拉伸伸长率 | Break,23℃ | ASTM D638 | 40 | % | |
| 弯曲模量 | 23°C | ASTM D790 | 2650 | MPa | |
| 弯曲强度 | 23°C | ASTM D790 | 91.0 | MPa | |
| 剪切强度 | 2.00mm | ASTM D732 | 55.0 | MPa | |
| Izod缺口冲击强度 | 3.20mm | ASTM D256 | 59.0 | J/m | |
| 电气性能 | 表面电阻率 | ASTM D257 | 1.0E+16 | ohms | |
| 体积电阻率 | ASTM D257 | 1.0E+14 | ohm·cm | ||
| 电气强度 | ASTM D149 | 19 | kV/mm | ||
| 介电常数 | 1E+6 Hz | ASTM D150 | 3.70 | ||
| 介质损耗因数 | 1E+6 Hz | ASTM D150 | 0.0070 | ||
| 热性能 | 热畸变温度 | 0.45MPa,未退火 | ASTM D648 | 158 | °C |
| 热畸变温度 | ASTM D648 | 110 | °C | ||
| 熔融温度 | 165 | °C | |||
| 线性热膨胀系数 | flow,20 to 80°C | ASTM D696 | 0.00013 | cm/cm/°C | |
| 其它性能 | 阻燃等级 | 0.8mm | UL 94 | HB | |