NEOFLON™ AP-210
全氟烷氧基
DAIKIN AMERICA, INC.
产品说明：
NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.
NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.
NEOFLON™ AP-210 物性表
基本信息
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
物理性能额定值单位制测试方法
| 比重 | 2.14 到 2.16 | g/cm³ | ASTM D792 |
| 表观密度 | 1.00 到 1.40 | g/cm³ | JIS K6891 |
| 熔流率（熔体流动速率） (372°C/5.0 kg) | 10 到 17 | g/10 min | ASTM D1238 |
| 吸水率 (饱和) | < 0.010 | % | ASTM D570 |
硬度额定值单位制测试方法
| 肖氏硬度 (邵氏 D) | 60 到 70 | ASTM D2240 |
机械性能额定值单位制测试方法
| 抗张强度 (屈服) | 25.4 到 30.4 | MPa | JIS K6891 |
| 伸长率 (断裂) | 350 到 450 | % | JIS K6891 |
| 弯曲模量 | 580 到 690 | MPa | ASTM D790 |
| 压缩模量 | 490 到 590 | MPa | ASTM D695 |
| 压缩强度 | ASTM D695 | ||
| 1% 应变 | 4.90 到 5.90 | MPa | ASTM D695 |
| 25% 应变 | 31.4 到 33.3 | MPa | ASTM D695 |
| 摩擦系数 (与钢 - 静态) | 0.040 到 0.050 | ||
| 负载变形 | ASTM D621 | ||
| 25°C, 14 MPa 1 | 8.00 到 9.00 | % | ASTM D621 |
| 25°C, 14 MPa 2 | 2.50 到 3.00 | % | ASTM D621 |
| 100°C, 6.9 MPa 3 | 8.50 到 9.50 | % | ASTM D621 |
| 100°C, 6.9 MPa 4 | 2.00 到 3.00 | % | ASTM D621 |
| Flexural Strength | No break | ASTM D790 |
冲击性能额定值单位制测试方法
| 悬壁梁缺口冲击强度 | 无断裂 | ASTM D256 |
热性能额定值单位制测试方法
| 熔融温度 | 300 到 310 | °C | ASTM D4591 |
| 线形热膨胀系数 - 流动 (20 到 100°C) | 1.2E-4 | cm/cm/°C | ASTM D696 |
| 比热 | 1050 | J/kg/°C | |
| 导热系数 | 0.26 | W/m/K | ASTM C177 |
可燃性额定值单位制测试方法
| UL 阻燃等级 (1.57 mm) | V-0 | UL 94 | |
| 极限氧指数 (1.57 mm) | > 95 | % | ASTM D2863 |
充模分析额定值单位制
| 熔体粘度 (380°C) | 2.00E+6 到 2.50E+7 | mPa·s |
备注
| 1 . | Total deformation |
| 2 . | Compressive creep |
| 3 . | Total deformation |
| 4 . | Compressive creep |