| 厂家(产地) | 台湾奇美 |
|---|---|
| 牌号 | PA-756H |
| 加工级别 | 注塑级 |
| 特性级别 | 高抗冲,高流动 |
| 用途级别 | 通用级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 75 | g/10min |
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 8.5 | g/10min | |
| 比重 | ASTM D-792 | 1.05 | 23/23℃ | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 115 | R | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 1.9 | ft.lb/in | |
| 弯曲弹性率 | ASTM D-790 | 2.3×104 | kg/cm2 | ||
| 引张强度 | ASTM D-638 | 400 | kg/cm2 | ||
| 引张强度 | ASTM D-638 | 5670 | lb/in2 | ||
| 弯曲强度 | ASTM D-790 | 9070 | lb/in2 | ||
| IZOD冲击强度 | 1/4" | ASTM D-256 | 1.5 | ft.lb/in | |
| 弯曲强度 | ASTM D-790 | 640 | kg/cm2 | ||
| 伸长率 | ASTM D-638 | 10 | % | ||
| IZOD冲击强度 | 1/4" | ASTM D-256 | 8 | kg.cm/cm | |
| 弯曲弹性率 | ASTM D-790 | 3.2×105 | lb/in2 | ||
| IZOD冲击强度 | 200℃×5kg | ASTM D-256 | 10 | kg.cm/cm | |
| 热性能 | 热变形温度 | ASTM D-648 | 99(210) | ℃ | |
| 燃烧性 | File No. E56070 UL&C-UL | 1/16"HB | |||
| 维卡软化点 | ASTM D-1525 | 221 | ℉ | ||
| 热变形温度 | ASTM D-648 | 89(192) | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 105 | ℃ | ||
ABS树脂是五大合成树脂之一，其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良，还具有易加工、制品尺寸稳定、表面光泽性好等特点，容易涂装、着色，还可以进行表面喷镀金属、电镀、焊接、热压和粘接等二次加工，广泛应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域，是一种用途极广的热塑性工程塑料。ABS外观为不透明呈象牙色粒料，其制品可着成五颜六色，并具有高光泽度。ABS相对密度为1.05G/CM3左右，吸水率低。ABS同其他材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18～20，属易燃聚合物，火焰呈黄色，有黑烟，并发出特殊的臭味