| 厂家(产地) | 台湾长春 |
|---|---|
| 牌号 | 3015NC |
| 加工级别 | 注塑级 |
| 特性级别 | 增强级 |
| 用途级别 | 纤维 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 吸湿率 | 24h | ASTM D570 | 0.04 | % | |
| 玻璃纤维含量 | 15 | % | ||||
| 比重 | ASTM D792 | 1.41 | ||||
| 机械性能 | 挠曲强度 | ASTM D790 | 1500 | kg/cm2 | ||
| 挠曲模数 | ASTM D790 | 50000 | kg/cm2 | |||
| 引张伸长率 | ASTM D638 | 4.0 | % | |||
| 冲击强度 | ASTM D256 | 6.0 | kg.cm/cm | |||
| 硬度 | ASTM D785 | 90 | M | |||
| 引张强度 | ASTM D638 | 950 | kg/cm2 | |||
| 电气性能 | 体积抵抗率 | ASTM D257 | 1015 | Ω.cm | ||
| 表面抵抗率 | ASTM D257 | 1013 | Ω | |||
| 诱电正接 | ASTM D150 | 0.001 | 60Hz | |||
| 介电常数 | ASTM D150 | 3.5 | 60Hz | |||
| 绝缘破坏强度 | 2mm | ASTM D149 | 20 | KV/mm | ||
| 耐电弧性 | ASTM D495 | 120 | SEC | |||
| 热性能 | 熔点 | DSC | 225 | ℃ | ||
| 热变形温度 | - | 18.6kg/cm2 | ASTM D648 | 200 | ℃ | |
| - | 4.6kg/cm2 | ASTM D648 | 220 | ℃ | ||
| 热膨胀系数 | ASTM D696 | 5 | 10-5cm/cm℃ | |||
| 耐燃性 | UL94 | HB | ||||
产品牌号：PBT/台湾长春/3015NC
产品简介：聚对苯二甲酸丁二醇酯.英文名polybutylene terephthalate(简称PBT).属于聚酯系列.PBT工程塑料是一种热塑性聚酯.非增强型的PBT与其它热塑性工程塑料相比.加工性能和电性能较好.PBT玻璃化温度低.模具温度在50℃时即可迅速结晶.加工周期短.聚对苯二甲酸丁二醇酯(PBT)被广泛应用于电子.电气和汽车工业中。
产品信息：PBT为乳白色半透明到不透明.结晶型热塑性聚酯.具有高耐热性、韧性、耐疲劳性.自润滑.低摩擦系数.耐候性.吸水率低.仅为0.1%.在潮湿环境中仍保持各种物性(包括电性能).电绝缘性.但体积电阻.介电损耗大.耐热水.碱类.酸类.油类.但易受卤化烃侵蚀.耐水解性差.低温下可迅速结晶.成型性良好。
工艺条件：干燥处理：这种材料在高温下很容易水解，因此加工前的干燥处理是很重要的。建议在空气中的干燥条件为120℃，6~8小时，或者150℃，2~4小时。湿度必须小于0.03%。如果用吸湿干燥器干燥，建议条件为150℃，2.5小时。熔化温度：225~275℃，建议温度：250℃ 。模具温度：对于未增强型的材料为40~60℃。要很好地设计模具的冷却腔道以减小塑件的弯曲。热量的散失一定要快而均匀。建议模具冷却腔道的直径为12mm。注射压力：中等（**大到1500bar）。注射速度：应使用尽可能快的注射速度（因为PBT的凝固很快）。流道和浇口:建议使用圆形流道以增加压力的传递（经验公式：流道直径=塑件厚度+1.5mm）。可以使用各种型式的浇口。也可以使用热流道，但要注意防止材料的渗漏和降解。浇口直径应该在0.8~1.0*t之间，这里 t是塑件厚度。如果是潜入式浇口，建议**小直径为0.75mm。