| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 10 | g/10min | |
| 平衡吸水率 | 23℃，相对湿度50% | ASTM D-570 | 0.32 | % | ||
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1200 | kg/m3 | ||
| 阻燃等级 | 3.2mm | UL 94 | HB | |||
| 折射率 | ASTM D-542 | 1.586 | ||||
| 模具收缩率 | ASTM D-955 | 0.005-0.007 | in/in | |||
| 透光率 | ASTM D-1003 | 89 | % | |||
| 雾度 | ASTM D-1003 | 0.7-1.5 | % | |||
| 阻燃等级 | 1.6mm | UL 94 | HB | |||
| 机械性能 | 伸长率 | 屈服点 | ASTM D-638 | 6 | % | |
| 断裂点 | ASTM D-638 | 150 | % | |||
| 落锤冲击强度 | 总能量@23℃ | ASTM D-3763 | 87 | J | ||
| 弯曲模量 | ASTM D-790 | 2410 | MPa | |||
| 洛氏硬度 | ASTM D-785 | 73 | M标度 | |||
| 洛氏硬度 | ASTM D-785 | 118 | R标度 | |||
| 弯曲强度 | ASTM D-790 | 96 | MPa | |||
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | j/m | ||
| 拉伸模量 | ASTM D-638 | 2410 | MPa | |||
| 拉伸强度 | 屈服点 | 50mm/min | ASTM D-638 | 60 | MPa | |
| 断裂点 | - | ASTM D-638 | 71 | MPa | ||
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | j/m | ||
| 电气性能 | 损耗因素 | 60Hz | ASTM D-150 | 0.001 | ||
| 介电强度 | 60Hz | ASTM D-149 | 17 | V/mil | ||
| 辉光灯丝测试 | 2mm，5s | IEC 695-2-1 | 850 | ℃ | ||
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | V | ||
| 体积电阻 | 23℃，干 | ASTM D-257 | 2.0×1017 | Ω.cm | ||
| 热性能 | 球状压痕温度 | IEC 598-1 | >125 | ℃ | ||
| 平均燃烧系数 | ASTM D-635 | 25 | mm | |||
| 热变形温度 | 退火@0.45MPa | ASTM D-648 | 144 | ℃ | ||
| 维卡软化点 | 50℃/小时，50n重 | ASTM D-1525 | 149 | ℃ | ||
| 热变形温度 | 未退火@1.82MPa | ASTM D-648 | 128 | ℃ | ||
| 线性热收缩率 | -40℃～82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ | ||
| 热变形温度 | 退火@1.82MPa | ASTM D-648 | 141 | ℃ | ||
| 其它性能 | 需氧系数 | ASTM D-2863 | 26 | % | ||