| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 1 | g/10min |
| 熔体流动速率 | 220℃/10kg | ASTM D-1238 | 11 | g/10min |
| 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 3 | g/10min |
| 比重 | ASTM D-792 | 1.02 | g/cc | |
| 成型收缩率 | ASTM D-955 | 0.4-0.7 | % | |
| 拉伸强度 | 50mm/min | ASTM D-638 | 380 | kg/cm2 |
| 拉伸模量 | 1mm/min | ASTM D-638 | 17200 | kg/cm2 |
| 屈服伸长率 | 50mm/min | ASTM D-638 | 6 | % |
| 断裂伸长率 | 50mm/min | ASTM D-638 | 25 | % |
| 弯曲强度 | 15mm/min | ASTM D-790 | 595 | kg/cm2 |
| 弯曲模量 | 15mm/min | ASTM D-790 | 19300 | kg/cm2 |
| IZOD缺口冲击强度 | 1/4" 23℃ | ASTM D-256 | 52 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/4" -30℃ | ASTM D-256 | 31 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/8" 23℃ | ASTM D-256 | 51 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/8" -30℃ | ASTM D-256 | 34 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 94 | R-scale | |
| 热变形温度 | 18.5kg/cm21/4"退火 | ASTM D-648 | 92 | ℃ |
| 热变形温度 | 18.5kg/cm21/4"未退火 | ASTM D-648 | 85 | ℃ |
| 热变形温度 | 4.6kg/cm21/4"退火 | ASTM D-648 | 92 | ℃ |
| 热变形温度 | 4.6kg/cm21/4" 未退火 | ASTM D-648 | 89 | ℃ |
| 维卡软化点 | 5kg 50℃/h | ASTM D-1525 | 93 | ℃ |
| 阻燃等级 | 1/8" | UL94 | HB | calss |
| 阻燃等级 | 1/16" | UL94 | HB | calss |