| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 24hrs | ASTM D-570 | 0.06 | % | |
| 物理性能 | 阻燃性 | UL 94 | 0.8 | mm | ||
| 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 | ||
| 阻燃性 | UL 94 | V-0 | ||||
| 比重 | ASTM D-792 | 1.11 | ||||
| 机械性能 | 缺口冲击强度 | 23°C | ASTM D-256 | 160 | J/M | |
| 拉伸强度 | 屈服点 | 3.2mm | ASTM D-638 | 75 | MPa | |
| 断裂点 | 3.2mm | ASTM D-638 | 18 | MPa | ||
| 弯曲强度 | 6.4mm | ASTM D-790 | 112 | MPa | ||
| 弯曲模量 | 6.4mm | ASTM D-790 | 2646 | MPa | ||
| 电气性能 | 介电常数 | 1MHz | ASTM D-150 | 2.49 | ||
| 体积电阻率 | ASTM D-257 | 2.0×1016 | Ω.cm | |||
| 表面电阻率 | ASTM D-257 | 1.0×1016 | Ω.cm | |||
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 133 | °C | |
| UL长期使用温度 | 电气 | UL 746B | 105 | °C | ||
| 含冲击 | UL 746B | 100 | °C | |||
| 无冲击 | UL 746B | 105 | °C | |||
| 维卡软化点 | ASTM D-1525 | 150 | °C | |||
| 热变形温度 | 1.8MPa | ASTM D-648 | 122 | °C | ||