| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 230℃,2.16kg | ASTM D-1238 | 8 | g/10min |
| 密度 | ASTM D-1505 | 0.91 | g/cm3 | ||
| 物理性能 | 模具收缩率 | 2mm(t) | 1.5-1.8 | % | |
| 机械性能 | 抗张强度(屈服) | 50mm/min | ASTM D-638 | 360 | kg/cm2 |
| IZOD冲击强度 | 1/4",23℃ | ASTM D-256 | 3 | kg·cm/cm | |
| 弯曲模量 | ASTM D-790 | 16000 | kg/cm2 | ||
| 洛氏硬度 | 23℃ | ASTM D-785 | 110 | R scale | |
| 断裂伸长率 | 50mm/min | ASTM D-638 | 500 | % | |
| 抗张强度(断裂) | 50mm/min | ASTM D-638 | 250 | kg/cm2 | |
| 热性能 | 熔点 | SGC | DSC | 161 | |
| 可燃性 | 1/8" | UL 94 | HB | ||
| 热变形温度 | 18.6kg/cm2(1/8") | ASTM D-648 | 65 | ℃ | |
| 热变形温度 | 4.6kg/cm2(1/8 | ASTM D-648 | 155 | ℃ | |
| 维卡软化点 | 1kg | ASTM D-1525 | 155 | ||
| 可燃性 | 1/16" | UL 94 | HB | ||