牌号 :	101L NC010	加工级别 :	注塑级
特性级别 :	增强级	用途级别 :	通用级
品牌 :	美国杜邦

DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 (Unverified Data)**

Polymer,Thermoplastic,Nylon,Nylon 66

DuPont Performance Polymers

产品说明:

Unreinforced Polyamide 66

Zytel 101L NC010 is a lubricated polyamide 66 resin for injection molding.

Information provided by DuPont Performance Polymers

]

DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 (Unverified Data**) 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	0.970 g/cc	0.0350 lb/in³
	1.14 g/cc	0.0412 lb/in³	DAM; ISO 1183
吸水率	8.5 % @Thickness 2.00 mm	8.5 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
水分吸收	2.60 % @Thickness 2.00 mm	2.60 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
粘度	42820 cP @Shear Rate 5000 1/s, Temperature 300 °C	42820 cP @Shear Rate 5000 1/s, Temperature 572 °F	ISO 11403-1 -2
	51190 cP @Shear Rate 5000 1/s, Temperature 290 °C	51190 cP @Shear Rate 5000 1/s, Temperature 554 °F	ISO 11403-1 -2
	61310 cP @Shear Rate 5000 1/s, Temperature 280 °C	61310 cP @Shear Rate 5000 1/s, Temperature 536 °F	ISO 11403-1 -2
	72990 cP @Shear Rate 500 1/s, Temperature 300 °C	72990 cP @Shear Rate 500 1/s, Temperature 572 °F	ISO 11403-1 -2
	95840 cP @Shear Rate 500 1/s, Temperature 290 °C	95840 cP @Shear Rate 500 1/s, Temperature 554 °F	ISO 11403-1 -2
	127400 cP @Shear Rate 500 1/s, Temperature 280 °C	127400 cP @Shear Rate 500 1/s, Temperature 536 °F	ISO 11403-1 -2
粘度测试	150 cm³/g	150 cm³/g	DAM; ISO 307 1157 1628
线性成型收缩率,Flow	0.014 cm/cm	0.014 in/in	DAM; ISO 294-4 2577
线性成型收缩率，横向	0.014 cm/cm	0.014 in/in	DAM; ISO 294-4 2577

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（M 级）	59	59	50%RH; ISO 2039-2
	79	79	DAM; ISO 2039-2
洛氏硬度（R 级）	108	108	50%RH; ISO 2039-2
	121	121	DAM; ISO 2039-2
硬度，H358/30	85.0 MPa	12300 psi	50%RH; ISO 2039-1
	180 MPa	26100 psi	DAM; ISO 2039-1
抗张强度	2.00 MPa @Strain 0.135 %, Time 3600 sec	290 psi @Strain 0.135 %, Time 1.00 hour	50%RH; isochronous; ISO 11403-1 -2
	2.00 MPa @Strain 0.157 %, Time 36000 sec	290 psi @Strain 0.157 %, Time 10.0 hour	50%RH; isochronous; ISO 11403-1 -2
	2.00 MPa @Strain 0.192 %, Time 360000 sec	290 psi @Strain 0.192 %, Time 100 hour	50%RH; isochronous; ISO 11403-1 -2
	2.00 MPa @Strain 0.305 %, Time 3.60e+7 sec	290 psi @Strain 0.305 %, Time 10000 hour	50%RH; isochronous; ISO 11403-1 -2
	2.00 MPa @Strain 0.239 %, Time 3.60e+6 sec	290 psi @Strain 0.239 %, Time 1000 hour	50%RH; isochronous; ISO 11403-1 -2
	12.0 MPa @Strain 1.95 %, Time 3.60e+6 sec	1740 psi @Strain 1.95 %, Time 1000 hour	50%RH; isochronous; ISO 11403-1 -2
	12.0 MPa @Strain 2.50 %, Time 3.60e+7 sec	1740 psi @Strain 2.50 %, Time 10000 hour	50%RH; isochronous; ISO 11403-1 -2
	12.0 MPa @Strain 1.52 %, Time 360000 sec	1740 psi @Strain 1.52 %, Time 100 hour	50%RH; isochronous; ISO 11403-1 -2
	12.0 MPa @Strain 1.25 %, Time 36000 sec	1740 psi @Strain 1.25 %, Time 10.0 hour	50%RH; isochronous; ISO 11403-1 -2
	12.0 MPa @Time 3600 sec, Strain 1.02 %	1740 psi @Time 1.00 hour, Strain 1.02 %	50%RH; isochronous; ISO 11403-1 -2
	24.0 MPa @Time 3600 sec, Strain 3.29603 %	3480 psi @Time 1.00 hour, Strain 3.29603 %	50%RH; isochronous; ISO 11403-1 -2
	24.0 MPa @Strain 3.91667 %, Time 36000 sec	3480 psi @Strain 3.91667 %, Time 10.0 hour	50%RH; isochronous; ISO 11403-1 -2
抗张强度(屈服)	55.0 MPa	7980 psi	50%RH; ISO 527-1/-2
	82.0 MPa	11900 psi	DAM; ISO 527-1/-2
伸长率 (断裂)	25 %	25 %	DAM; Nominal; ISO 527-1/-2
	>= 50 %	>= 50 %	50%RH; Nominal; ISO 527-1/-2
屈服伸长率	4.5 %	4.5 %	DAM; ISO 527-1/-2
	4.5 %	4.5 %	DAM; ISO 527-3
	25 %	25 %	50%RH; ISO 527-1/-2
拉伸模量	1.40 GPa	203 ksi	50%RH; ISO 527-1/-2
	3.10 GPa	450 ksi	DAM; ISO 527-1/-2
	0.373 GPa @Temperature 120 °C	54.1 ksi @Temperature 248 °F	50%RH; ISO 11403-1 -2
	0.460 GPa @Temperature 120 °C	66.7 ksi @Temperature 248 °F	DAM; ISO 11403-1 -2
	0.945 GPa @Temperature 40.0 °C	137 ksi @Temperature 104 °F	50%RH; ISO 11403-1 -2
	2.769 GPa @Temperature 40.0 °C	401.6 ksi @Temperature 104 °F	DAM; ISO 11403-1 -2
	3.555 GPa @Temperature -40.0 °C	515.6 ksi @Temperature -40.0 °F	DAM; ISO 11403-1 -2
	4.493 GPa @Temperature -40.0 °C	651.7 ksi @Temperature -40.0 °F	50%RH; ISO 11403-1 -2
弯曲模量	1.20 GPa	174 ksi	50%RH; ISO 178
	2.80 GPa	406 ksi	DAM; ISO 178
剪切模量	0.154 GPa @Temperature 160 °C	22.3 ksi @Temperature 320 °F	50%RH; Dynamic; ISO 11403-1 -2
	0.160 GPa @Temperature 160 °C	23.2 ksi @Temperature 320 °F	DAM; Dynamic; ISO 11403-1 -2
	0.180 GPa @Temperature 120 °C	26.1 ksi @Temperature 248 °F	DAM; Dynamic; ISO 11403-1 -2
	0.180 GPa @Temperature 120 °C	26.1 ksi @Temperature 248 °F	50%RH; Dynamic; ISO 11403-1 -2
	0.240 GPa @Temperature 70.0 °C	34.8 ksi @Temperature 158 °F	50%RH; Dynamic; ISO 11403-1 -2
	0.335 GPa @Temperature 70.0 °C	48.6 ksi @Temperature 158 °F	DAM; Dynamic; ISO 11403-1 -2
	0.880 GPa @Temperature 20.0 °C	128 ksi @Temperature 68.0 °F	50%RH; Dynamic; ISO 11403-1 -2
	0.919 GPa @Temperature 20.0 °C	133 ksi @Temperature 68.0 °F	DAM; Dynamic; ISO 11403-1 -2
	1.02 GPa @Temperature -20.0 °C	148 ksi @Temperature -4.00 °F	DAM; Dynamic; ISO 11403-1 -2
	1.04 GPa @Temperature -20.0 °C	151 ksi @Temperature -4.00 °F	50%RH; Dynamic; ISO 11403-1 -2
	1.11 GPa @Temperature -50.0 °C	161 ksi @Temperature -58.0 °F	DAM; Dynamic; ISO 11403-1 -2
	1.15 GPa @Temperature -50.0 °C	167 ksi @Temperature -58.0 °F	50%RH; Dynamic; ISO 11403-1 -2
悬壁梁缺口冲击强度	5.50 kJ/m²	2.62 ft-lb/in²	DAM; ISO 180/1A
	12.0 kJ/m²	5.71 ft-lb/in²	50%RH; ISO 180/1A
	3.00 kJ/m² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 180/1A
	5.50 kJ/m² @Temperature -40.0 °C	2.62 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 180/1A
	5.50 kJ/m² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 180/1A
悬壁梁无缺口冲击强度	NB	NB	DAM; ISO 180/1U
	NB	NB	50%RH; ISO 180/1U
	300 kJ/m² @Temperature -30.0 °C	143 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 180/1U
简支梁无缺口冲击强度	NB	NB	DAM; ISO 179/1eU
	NB	NB	50%RH; ISO 179/1eU
	40.0 J/cm² @Temperature -30.0 °C	190 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F