| 牌号 : | 900p | 加工级别 : | 注塑级 |
| 特性级别 : | 增强级,耐磨,高强度,高流动,高抗冲,高刚性 | 用途级别 : | 填充级,纤维,薄壁制品 |
| 品牌 : | 美国陶氏杜邦 | 厂家(产地) : | 美国杜邦 |
| 销售方式 : | 品牌经销 | 类型 : | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.42 | ||
| 模收缩 | 2.2-2.4 | ||||
| 吸水量 | 50相对湿度 | ASTM D-570 | 0.22 | ||
| 吸水量 | 浸渍平衡点 | ASTM D-570 | 0.90 | ||
| 吸水量 | 24小时浸渍 | ASTM D-570 | 0.25 | ||
| 机械性能 | 洛氏硬度M | ASTM D-785 | 94 | ||
| 挠曲系数 | 23 | ||||
| ASTM D-790 | 3220 | MPa | |||
| 挠曲系数 | 100 | ||||
| ASTM D-790 | 1030 | MPa | |||
| 洛氏硬度R | ASTM D-785 | 120 | |||
| 破裂点拉伸变形量 | 23 | ||||
| ASTM D-638 | 25 | ||||
| IZOD冲击强度 | 23 | ||||
| ASTM D-256 | 71 | j/m | |||
| 抗拉伸冲击强度 | 长试片23 | ||||
| ASTM D-1822 | 250 | kj/m2 | |||
| 挠曲系数 | 70 | ||||
| ASTM D-790 | 1720 | MPa | |||
| IZOD冲击强度 | 缺口-40 | ||||
| ASTM D-256 | 55 | j/m | |||
| 拉伸强度 | 70 | ||||
| ASTM D-638 | 48 | MPa | |||
| 挠曲疲劳忍耐限度 | 50RH,23,106周期 | ASTM D-671 | 32 | MPa | |
| 破裂点拉伸变形量 | -55 | ||||
| ASTM D-638 | 10 | ||||
| 压缩应力 | 23,10变形 | ASTM D-695 | 121 | MPa | |
| 破裂点拉伸变形量 | 70 | ||||
| ASTM D-638 | 180 | ||||
| 破裂点拉伸变形量 | 100 | ||||
| ASTM D-638 | >260 | ||||
| 挠曲系数 | -55 | ||||
| ASTM D-790 | 4730 | MPa | |||
| 拉伸强度 | 23 | ||||
| ASTM D-638 | 69 | MPa | |||
| 弹性系数 | 23 | ||||
| ASTM D-638 | 3640 | MPa | |||
| 抗剪强度 | 23 | ||||
| ASTM D-732 | 66 | MPa | |||
| 挠曲系数 | 122 | ||||
| ASTM D-790 | 755 | MPa | |||
| 破裂点拉伸变形量 | 122 | ||||
| ASTM D-638 | >260 | ||||
| 挠曲变形强度 | 23 | ||||
| ASTM D-790 | 97 | MPa | |||
| 拉伸强度 | 122 | ||||
| ASTM D-638 | 26 | MPa | |||
| IZOD冲击强度 | 无缺口23 | ||||
| ASTM D-256 | 1620 | j/m | |||
| 拉伸强度 | 100 | ||||
| ASTM D-638 | 36 | MPa | |||
| 负载变形量 | 140kg/cm2,50 | ||||
| ASTM D-621 | 0.5 | ||||
| 压缩应力 | 23,1变形 | ASTM D-695 | 35 | MPa | |
| 拉伸强度 | -55 | ||||
| ASTM D-638 | 101 | MPa | |||
| 电气性能 | 介电强度 | 瞬间Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm |
| 容积电阻率 | 23,0.2含水量 | ASTM D-257 | 1×1015 | Ω.cm | |
| 抗电弧 | 3.1mm | ASTM D-495 | 220 | sec | |
| 介电常数 | 50RH,23,102106Hz | ASTM D-150 | 3.7 | Ω.cm | |
| 介电因数 | 50RH,23,106Hz | ASTM D-150 | 0.005 | ||
| 热性能 | 线性热膨胀系数 | 2960 | |||
| ASTM D-696 | 12.2 | 10-5m/m | |||
| 自燃性 | UL 94 | HB | |||
| 热传导系数 | 0.37 | W/mk | |||
| 线性热膨胀系数 | 60104 | ||||
| ASTM D-696 | 13.7 | 10-5m/m | |||
| 线性热膨胀系数 | 104160 | ||||
| ASTM D-696 | 14.9 | 10-5m/m | |||
| 热畸变温度 | 1.8MPa | ASTM D-648 | 136 | ||
| 热畸变温度 | 0.5MPa | ASTM D-648 | 172 | ||
| 线性热膨胀系数 | -4029 | ||||
| ASTM D-696 | 10.4 | 10-5m/m | |||
| 熔点 | |||||
| ASTM D-2133 | 175 | ||||