| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.03 | % | |
| 物理性能 | 玻璃纤维含量 | Ash | 30 | % | |
| 成型收缩率 | ASTM D-955 | 0.2-1.4 | % | ||
| 比重 | ASTM D-792 | 1.58-1.64 | |||
| 机械性能 | 引张强度 | ASTM D-638 | 1100-1400 | Kg/cm2 | |
| 挠曲弹性率 | ASTM D-790 | 70000-100000 | Kg/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 94 | M-Scale | ||
| IZOD冲击强度 | ASTM D-256 | 7.0-13.0 | Kg.cm/cm | ||
| 挠曲强度 | ASTM D-790 | 1500-2300 | Kg/cm2 | ||
| 引张伸长率 | ASTM D-638 | 4-5 | % | ||
| 电气性能 | 耐电弧性 | ASTM D-495 | 100 | sec | |
| 绝缘破坏强度 | ASTM D-149 | 23 | KV/mm | ||
| 表面电阻率 | ASTM D-257 | >1014 | Ω | ||
| 诱电正接 | 60Hz | ASTM D-150 | 0.001 | ||
| 体积电阻率 | ASTM D-257 | >1016 | Ω.cm | ||
| 诱电率 | 60Hz | ASTM D-150 | 3.5 | ||
| 热性能 | 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 208 | ℃ |
| 线膨胀系数 | ASTM D-696 | 3 | 10-5cm/cm℃ | ||
| 热变形温度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ | |
| 熔点 | DSC | 225 | ℃ | ||
| 耐燃性 | 3.0mm | UL 94 | V-0 | ||