| 类型 | 标准料 |
| 牌号 | 41H |
| 销售方式 | 品牌经销 |
| 颜色 | 本色 |
| 用途级别 | 汽车部件 |
| 品牌 | 美国首诺 |
| 厂家(产地) | 美国首诺 |
| 加工级别 | 注塑级 |
| 特性级别 | 高抗冲,耐低温 |
| 规格级别 | 热稳定 |
(温馨提示：因塑料行情每天都会有变更，页面上有些报价可能会与当天实际报价有所差异，仅供参考！价格以当天市场行情为准，欢迎来电咨询:18551114352/QQ：357201478)
Vydyne® 41H 聚酰胺66 Ascend Performance Materials Operations LLC 产品说明: Vydyne 41H is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 41H was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.
Vydyne 41H is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. 单位: 公制 | 英制 Properties 处理 资料 视觉搜索 曲线数据 购买地点
| 总体 | |
| 材料状态 | 已商用：当前有效 |
| 资料 1 | Technical Datasheet |
| UL 黄卡 2 | E70062-100757495 |
| 搜索 UL 黄卡 | | Ascend Performance Materials Operations LLC | Vydyne® | | |
| 供货地区 | |
| 添加剂 | 冲击改性剂 |
| 特性 | | 冲击改性 抗溶剂性 抗撞击性，高 | 可加工性，良好 良好耐磨损性 耐低温冲击 | 耐化学性良好 耐汽油性 耐油性能 | |
| 用途 | | 齿轮 电气/电子应用领域 工业应用 | 紧固件 连接器 汽车领域的应用 | 消费品应用领域 | |
| 机构评级 | | ASTM D 4066 PA0181 | ASTM D 6779 PA0181 | | |
| 外观 | 自然色 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.08 | -- | g/cm3 | ISO 1183 |
| 收缩率 | | | | ISO 294-4 |
| 垂直流动方向 : 2.00 mm | 1.6 | -- | % | |
| 流动方向 : 2.00 mm | 1.8 | -- | % | |
| 吸水率 | | | | ISO 62 |
| 23°C, 24 hr | 1.0 | -- | % | |
| 平衡, 23°C, 50% RH | 2.1 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 (23°C) | 1860 | 1390 | MPa | ISO 527-2 |
| 拉伸应力 | | | | ISO 527-2 |
| 屈服, 23°C | 50.0 | 35.0 | MPa | |
| 断裂, 23°C | 43.0 | 39.0 | MPa | |
| 拉伸应变 (断裂, 23°C) | 50 | 180 | % | ISO 527-2 |
| 弯曲模量 (23°C) | 1750 | 545 | MPa | ISO 178 |
| 弯曲应力 (23°C) | 53.0 | 17.0 | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | | | | ISO 179 |
| -40°C | 20 | 25 | kJ/m2 | |
| -30°C | 35 | 25 | kJ/m2 | |
| 23°C | 76 | 110 | kJ/m2 | |
| 简支梁无缺口冲击强度 | | | | ISO 179 |
| -30°C | 无断裂 | 无断裂 | | |
| 23°C | 无断裂 | 无断裂 | | |
| 悬壁梁缺口冲击强度 | | | | ISO 180 |
| -40°C | 22 | 25 | kJ/m2 | |
| -30°C | 40 | 29 | kJ/m2 | |
| 23°C | 78 | 88 | kJ/m2 | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 热变形温度 | | | | |
| 0.45 MPa, 未退火 | 145 | -- | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 58.0 | -- | °C | ISO 75-2/A |
| 熔融温度 | 260 | -- | °C | ISO 11357-3 |
| 线形热膨胀系数 | | | | ISO 11359-2 |
| 流动 : 23 到 55°C, 2.00 mm | 1.7E-4 | -- | cm/cm/°C | |
| 横向 : 23 到 55°C, 2.00 mm | 1.5E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI | | | | UL 746 |
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率 (0.750 mm) | 1.0E+10 | -- | ohms·cm | IEC 60093 |
| 介电强度 (1.00 mm) | 14 | -- | kV/mm | IEC 60243 |
| 耐电弧性 (3.00 mm) | PLC 6 | -- | | ASTM D495 |
| 漏电起痕指数 (3.00 mm) | 600 | -- | V | IEC 60112 |
| 高电弧燃烧指数(HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| 高电压电弧起痕速率 (HVTR) | PLC 2 | -- | | UL 746 |
| 热丝引燃 (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 3 | -- | | |
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| UL 阻燃等级 | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| 灼热丝易燃指数 | | | | IEC 60695-2-12 |
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| 热灯丝点火温度 | | | | IEC 60695-2-13 |
| 0.750 mm | 750 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| 补充信息 | 干燥 | 调节后的 | | 测试方法 |
| Automotive Materials - (thickness d = 1 mm) | + | -- | | FMVSS 302 |
| 注射 | 干燥 | 单位制 | |
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大回制料比例 | 25 | % | |
| 料筒后部温度 | 280 到 310 | °C | |
| 料筒中部温度 | 280 到 310 | °C | |
| 料筒前部温度 | 280 到 310 | °C | |
| 射嘴温度 | 280 到 310 | °C | |
| 加工（熔体）温度 | 285 到 305 | °C | |
| 模具温度 | 65.0 到 95.0 | °C | |