| 厂家(产地) | 台湾长春 |
|---|---|
| 牌号 | 3015 |
| 特性级别 | 增强级,耐高温 |
| 用途级别 | 纤维 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.04 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.39-1.43 | ||
| 玻璃纤维含量 | Ash | 15 | % | ||
| 成型收缩率 | ASTM D-955 | 0.2-1.4 | % | ||
| 机械性能 | IZOD冲击强度 | ASTM D-256 | 5-7 | Kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 93 | M-Scale | ||
| 引张伸长率 | ASTM D-638 | 4-5 | % | ||
| 挠曲强度 | ASTM D-790 | 1300-1500 | Kg/cm2 | ||
| 挠曲弹性率 | ASTM D-790 | 40000-50000 | Kg/cm2 | ||
| 引张强度 | ASTM D-638 | 800-1000 | Kg/cm2 | ||
| 电气性能 | 表面电阻率 | ASTM D-257 | >1014 | Ω | |
| 诱电正接 | 60Hz | ASTM D-150 | 0.001 | ||
| 绝缘破坏强度 | ASTM D-149 | 20 | KV/mm | ||
| 体积电阻率 | ASTM D-257 | >1016 | Ω.cm | ||
| 诱电率 | 60Hz | ASTM D-150 | 3.3 | ||
| 耐电弧性 | ASTM D-495 | 129 | sec | ||
| 热性能 | 热变形温度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ |
| 线膨胀系数 | ASTM D-696 | 5 | 10-5cm/cm℃ | ||
| 熔点 | DSC | 225 | ℃ | ||
| 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 206 | ℃ | |
| 耐燃性 | 0.83mm | UL 94 | HB | ||
产品牌号：PBT/台湾长春/3015
产品简介：聚对苯二甲酸丁二醇酯.英文名polybutylene terephthalate(简称PBT).属于聚酯系列.PBT工程塑料是一种热塑性聚酯.非增强型的PBT与其它热塑性工程塑料相比.加工性能和电性能较好.PBT玻璃化温度低.模具温度在50℃时即可迅速结晶.加工周期短.聚对苯二甲酸丁二醇酯(PBT)被广泛应用于电子.电气和汽车工业中。
产品信息：PBT为乳白色半透明到不透明.结晶型热塑性聚酯.具有高耐热性、韧性、耐疲劳性.自润滑.低摩擦系数.耐候性.吸水率低.仅为0.1%.在潮湿环境中仍保持各种物性(包括电性能).电绝缘性.但体积电阻.介电损耗大.耐热水.碱类.酸类.油类.但易受卤化烃侵蚀.耐水解性差.低温下可迅速结晶.成型性良好。
工艺条件：干燥处理：这种材料在高温下很容易水解，因此加工前的干燥处理是很重要的。建议在空气中的干燥条件为120℃，6~8小时，或者150℃，2~4小时。湿度必须小于0.03%。如果用吸湿干燥器干燥，建议条件为150℃，2.5小时。熔化温度：225~275℃，建议温度：250℃ 。模具温度：对于未增强型的材料为40~60℃。要很好地设计模具的冷却腔道以减小塑件的弯曲。热量的散失一定要快而均匀。建议模具冷却腔道的直径为12mm。注射压力：中等（**大到1500bar）。注射速度：应使用尽可能快的注射速度（因为PBT的凝固很快）。流道和浇口:建议使用圆形流道以增加压力的传递（经验公式：流道直径=塑件厚度+1.5mm）。可以使用各种型式的浇口。也可以使用热流道，但要注意防止材料的渗漏和降解。浇口直径应该在0.8~1.0*t之间，这里 t是塑件厚度。如果是潜入式浇口，建议**小直径为0.75mm。
021-80107851