| 厂家(产地) | 韩国韩华 |
|---|---|
| 牌号 | 2020 |
| 加工级别 | 注塑级 |
| 特性级别 | 透明级,增强级 |
| 用途级别 | 薄膜级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.926 | g/cc | ||
| 熔体流动速率 | ASTM D-1238 | 0.4 | g/10min | |||
| 机械性能 | 断裂拉伸强度 | ASTM D-638 | 185 | kg/cm2 | ||
| 断裂伸长率 | ASTM D-638 | 730 | % | |||
| 断裂伸长率 | MD | ASTM D-882 | 300 | % | ||
| TD | ASTM D-882 | 630 | % | |||
| 断裂伸长率 | MD | ASTM D-882 | 300 | % | ||
| TD | ASTM D-882 | 630 | % | |||
| 拉伸断裂强度 | MD | ASTM D-882 | 270 | kg/cm2 | ||
| TD | ASTM D-882 | 250 | kg/cm2 | |||
| 下降冲击强度 | ASTM D-1709 | 300 | g | |||
| 热性能 | 熔点 | ASTM D-1525 | 104 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 90 | ℃ | |||
| 其它性能 | 混浊度 | ASTM D-1009 | 6.0 | % | ||
| 醋酸乙烯含量 | HCC Method | 3.5 | Wt% | |||
| 厚度 | HCC | 0.06 | ㎜ | |||
| 拉伸抗热强度 | MD | ASTM D-1004 | 90 | ASTM D1004 | ||
| TD | ASTM D-1004 | 95 | ASTM D1004 | |||