| 类型 | 标准料 |
|---|---|
| 牌号 | 7140F |
| 销售方式 | 品牌经销 |
| 用途级别 | 薄膜级,食品级 |
| 厂家(产地) | 台湾塑胶 |
| 加工级别 | 吹膜级,吹塑级 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.934 | g/cm3 | ||
| VA含量 | 14 | % | ||||
| 熔体流动速率 | ASTM D-1238 | 0.7 | g/10min | |||
| 机械性能 | 拉力降伏强度 | ASTM D-638 | 70 | Kg/cm2 | ||
| 弯曲模量 | ASTM D-790 | 230 | Kg/cm2 | |||
| 拉力断裂强度 | MD | ASTM D-882B | 310 | Kg/cm2 | ||
| TD | ASTM D-882B | 280 | Kg/cm2 | |||
| 硬度 | ASTM D-2240 | 92 | Shore A | |||
| 摩擦系数 | ASTM D-1894 | >0.5 | ||||
| 抗撕裂性 | MD | ASTM D-1922 | 10 | N/mm | ||
| TD | ASTM D-1922 | 24 | N/mm | |||
| 拉力断裂伸长率 | ASTM D-638 | 750 | % | |||
| 硬度 | ASTM D-2240 | 40 | Shore D | |||
| 断裂伸长率 | MD | ASTM D-882B | 450 | % | ||
| TD | ASTM D-882B | 600 | % | |||
| 拉力断裂强度 | ASTM D-638 | 200 | Kg/cm2 | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 370 | Kg/cm2 | ||
| TD | ASTM D-882B | 420 | Kg/cm2 | |||
| 拉力降伏强度 | MD | ASTM D-882B | 50 | Kg/cm2 | ||
| TD | ASTM D-882B | 40 | Kg/cm2 | |||
| 落球冲击强度 | ASTM D-1709 | 620 | g | |||
| 热性能 | 软化点 | ASTM D-1525 | 75 | ℃ | ||
| 脆化温度 | ASTM D-746 | <-70 | ℃ | |||
| 熔点 | DSC | 90 | ℃ | |||
| 其它性能 | 浊度 | ASTM D-1003 | 3 | % | ||
| 光泽度 | 45℃ | ASTM D-2457 | 90 | % | ||
| 薄膜厚度 | 30-150 | μ | ||||