类型 | 正牌料 |
牌号 | 1140L4 |
销售方式 | 品牌经销 |
颜色 | 本色 |
用途级别 | 注塑级,运动器材,纤维,通用级,瓶盖专用料,家电部件,光学级,电子电器部件 |
品牌 | PPS |
厂家(产地) | 日本宝理 |
加工级别 | 注塑级,热熔级,挤出级 |
特性级别 | 标准级,阻燃级,增韧级,增强级,耐水解,耐磨,耐老化,高强度,高抗冲,高滑动,高刚性 |
规格级别 | 玻纤增强级 |
产品说明:
Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).
1140L4 物性表
基本信息 | |
| E107854-237739 |
填料/增强材料 | 玻璃纤维增强材料, 40% 填料按重量 |
特性 | 超高韧性 刚性,高 高强度 可焊接 良好的电气性能 耐化学性良好 耐热性,高 硬度高 阻燃性 |
用途 | 泵件 电气/电子应用领域 阀门/阀门部件 汽车领域的应用 外壳 |
RoHS 合规性 | 联系制造商 |
多点数据 | Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) |
物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | 1.65 | g/cm3 | ASTM D792, ISO 1183 |
特定体积 | 0.611 | cm3/g | ASTM D792 |
充模分析 | 额定值 | 单位制 | 测试方法 |
Specific Heat Capacity of Melt | 1500 | J/kg/°C | 内部方法 |
补充信息 | 额定值 | 单位制 | 测试方法 |
Specimen Thickness - Shrinkage | 3.18 | mm | 内部方法 |
物理性能 | 额定值 | 单位制 | 测试方法 |
收缩率 | | | |
流动 | 0.20 到 0.30 | % | ASTM D955 |
横向流动 | 0.50 到 0.70 | % | ASTM D955 |
垂直流动方向 | 0.40 到 0.60 | % | ISO 294-4 |
流动方向 | 0.20 到 0.60 | % | ISO 294-4 |
吸水率 (饱和, 23°C) | 0.020 | % | ISO 62 |
硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 | | | |
M 级 | 100 | | ASTM D785 |
M 计秤 | 100 | | ISO 2039-2 |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | | | |
-40°C | 14500 | MPa | ASTM D638 |
75°C | 11900 | MPa | ASTM D638 |
150°C | 4270 | MPa | ASTM D638 |
200°C | 3240 | MPa | ASTM D638 |
-- | 14700 | MPa | ISO 527-2/1A/1 |
抗张强度 | | | |
断裂, 23°C | 200 | MPa | ASTM D638 |
断裂 | 195 | MPa | ISO 527-2/1A/5 |
伸长率 | | | |
断裂, 23°C | 1.7 | % | ASTM D638 |
断裂 | 1.9 | % | ISO 527-2/1A/5 |
弯曲模量 (23°C) | 14500 | MPa | ISO 178 |
弯曲应力 1 | 285 | MPa | ISO 178 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | | | ISO 179/1eA |
-30°C | 10 | kJ/m2 | ISO 179/1eA |
23°C | 10 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度 | | | ISO 179/1eU |
-30°C | 53 | kJ/m2 | ISO 179/1eU |
23°C | 53 | kJ/m2 | ISO 179/1eU |
悬壁梁缺口冲击强度 | | | ISO 180/1A |
-30°C | 10 | kJ/m2 | ISO 180/1A |
23°C | 10 | kJ/m2 | ISO 180/1A |
无缺口伊佐德冲击强度 (23°C) | 34 | kJ/m2 | ISO 180/1U |
热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 | | | |
0.45 MPa, 退火 | 280 | °C | ASTM D648 |
1.8 MPa, 未退火 | 265 | °C | ASTM D648 |
1.8 MPa, 未退火 | 270 | °C | ISO 75-2/A |
8.0 MPa, 未退火 | 215 | °C | ISO 75-2/C |
玻璃转化温度 2 | 90.0 | °C | ISO 11357-2 |
熔融温度 3 | 280 | °C | ISO 11357-3 |
线形热膨胀系数 | | | ISO 11359-2 |
流动 | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
横向 | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
体积电阻率 | | | |
-- | 1.0E+16 | ohms·cm | ASTM D257 |
-- | > 1.0E+15 | ohms·cm | IEC 60093 |
介电强度 | 28 | kV/mm | IEC 60243-1 |
介电常数 | | | |
1 kHz | 3.50 | | ASTM D150 |
1 MHz | 3.50 | | ASTM D150 |
1 MHz | 4.60 | | IEC 60250 |
耗散因数 | | | |
1 kHz | 1.0E-3 | | ASTM D150 |
1 MHz | 1.0E-3 | | ASTM D150 |
1 MHz | 6.2E-3 | | IEC 60250 |
耐电弧性 | 134 | sec | ASTM D495 |
漏电起痕指数 | 125 | V | IEC 60112 |
可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | | | UL 94 |
0.380 mm | V-0 | | UL 94 |
1.50 mm | V-0 | | UL 94 |
3.00 mm | 5VA | | UL 94 |
极限氧指数 | 47 | % | ISO 4589-2 |
注射 | 额定值 | 单位制 | |
干燥温度 | 130 到 140 | °C | |
干燥时间 | 3.0 到 4.0 | hr | |
建议的最大水分含量 | 0.020 | % | |
料斗温度 | 20.0 到 30.0 | °C | |
料筒后部温度 | 290 到 300 | °C | |
料筒中部温度 | 310 到 320 | °C | |
料筒前部温度 | 330 到 340 | °C | |
射嘴温度 | 310 到 330 | °C | |
加工(熔体)温度 | 330 到 340 | °C | |
模具温度 | 140 到 160 | °C | |
注塑压力 | 50.0 到 100 | MPa | |
注射速度 | 快速 | | |
保压 | 30.0 到 70.0 | MPa | |
背压 | 0.00 到 3.00 | MPa | |
注射说明 |
Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
备注 |
1 . | Break |
2 . | 10°C/min |
3 . | 10°C/min |