PETG 韩国SK JN200挤出级 物性认证数据表
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | ||
| 断裂伸长率 | ASTM D412/ISO 527 | 340 | % | ||
| 拉伸模量 | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 拉伸屈服伸长率(延伸率) | ASTM D412/ISO 527 | % | |||
| 拉伸断裂伸长率(延伸率) | ASTM D412/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 18348 | kg/cm2(MPa)[Lb/in2] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 683 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | 105 | kg·cm/cm(J/M)ft·lb/in | ||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg/cm2(MPa)[Lb/in2] | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.23 | ||
| 成型收缩率 | ASTM D955 | 0.002-0.005 | % | ||
| 光学性能 | 折射率 | ASTM D542/ISO 489 | |||
| 透光率 | ASTM D1003/ISO 13468 | % | |||
| 模糊系数（Haze） | ISO 14782 | % | |||
| 其他 | 备注 | ||||
| 颜色 | |||||
| 特性 | 光泽高，搞撞击性强。 | ||||
| 用途 | |||||
SK PETG作为板材原料的介绍：PETG的另一个非常广的用途就是板材。用PETG制成的板材，抗冲击性能和韧性都非常突出，其抗冲击性能是改性聚丙烯酸酯类的3到10陪。这种板材易于印刷和再加工，且具有同类塑料板中较好的环保性能。PETG板材与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高 ，PETG 作为异型材应用：可成型管材或各种型材，其制品坚硬、透明、光泽好，受压不泛白，易于成型及后加工处理，符合环保要求，同时符合美国FDA关于食品接触标准，广泛应用于建筑装饰及材料。
SK PETG用于吹瓶领域：
PETG材料的晶莹剔透性决定了其必然会成为各类追求美观的商品盛装容器的受宠儿。PETG瓶有着传统聚酯饮料瓶所不具备的韧性，再加上抗摔性好，可以任意作表面修饰，对人体无毒，可经常接触，广泛的应用于各类液态商品的包装和盛装，并在医疗领域也有应用。