| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.51 | ||
| 吸收率 | 23℃ 60%RH | ASTM D-570 | 0.18 | % | |
| 熔体流动速率 | ASTM D-1238 | 5 | g/10min | ||
| 伸长率 | 23℃ | ASTM D-638 | 15 | % | |
| 成型收缩率 | t3mm 直径100mm | 2.1 | % | ||
| 机械性能 | 拉伸冲击强度 | t3.2mm Stype | ASTM D-1822 | 40 | kgf.cm/cm2 |
| 拉伸强度 | 23℃ | ASTM D-638 | 440 | kgf/cm2 | |
| 断裂强度 | t2mm | ASTM D-732 | 421 | kgf/cm2 | |
| Izod缺口冲击强度 | Notch t3.2mm | ASTM D-256 | 4.0 | kgf.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 70 | M | ||
| 弯曲弹性率 | 23℃ | ASTM D-790 | 2.00×104 | kgf/cm2 | |
| 弯曲强度 | 23℃ | ASTM D-790 | 650 | kgf/cm2 | |
| 电气性能 | 耐电压 | ASTM D-149 | 16 | KV/mm | |
| 导电率 | 106Hz | ASTM D-150 | 3.1 | ||
| 体积电阻率 | ASTM D-257 | 1×1014 | Ω.cm | ||
| 个质损耗系数 | 106Hz | ASTM D-150 | 0.009 | ||
| 表面电阻率 | ASTM D-257 | 1×1016 | Ω | ||
| 热性能 | 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 156 | ℃ |
| 熔点 | 10℃/min | DSC Method | 165 | ℃ | |
| 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 106 | ℃ | |
| 线性膨胀系数 | 20℃ -80℃ | ASTM D-696 | 13×10-5 | mm/mm/℃ | |
| 阻燃性 | t0.8mm | UL-94 | HB | ||