| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | 23/23℃ | |
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 7.6 | g/10min | |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 70 | g/10min | |
| 机械性能 | 引张强度 | ASTM D-638 | 370 | kg/cm2 | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 18 | kg.cm/cm | |
| 弯曲弹性率 | ASTM D-790 | 2.4×104 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 8520 | lb/in2 | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 20 | kg.cm/cm | |
| 引张强度 | ASTM D-638 | 5250 | lb/in2 | ||
| 伸长率 | ASTM D-638 | 30 | % | ||
| 洛氏硬度 | ASTM D-785 | 113 | R | ||
| 弯曲弹性率 | ASTM D-790 | 3.4×105 | lb/in2 | ||
| IZOD冲击强度 | 220℃×10kg | ASTM D-256 | 3.3 | ft.lb/in | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 3.7 | ft.lb/in | |
| 弯曲强度 | ASTM D-790 | 600 | kg/cm2 | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 105 | ℃ | |
| 热变形温度 | ASTM D-648 | 99(210) | ℃ | ||
| 燃烧性 | File No. E56070 UL&C-UL | 1/16"HB | |||
| 热变形温度 | ASTM D-648 | 89(192) | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 221 | ℉ | ||