| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 7.5 | g/10min |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | ||
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 0.7 | g/10min | |
| 机械性能 | 弯曲强度 | ASTM D-790 | 620 | Kg/cm2 | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 6.5 | ft.lb/in | |
| 洛氏硬度 | ASTM D-785 | 102 | R | ||
| 引张强度 | ASTM D-638 | 5530 | lb/in2 | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 40 | kg.cm/cm | |
| 弯曲强度 | ASTM D-790 | 8800 | lb/in2 | ||
| 弯曲弹性率 | ASTM D-790 | 3.0×105 | lb/in2 | ||
| 引张强度 | ASTM D-638 | 390 | Kg/cm2 | ||
| 弯曲弹性率 | ASTM D-790 | 2.1×104 | Kg/cm2 | ||
| 伸长率 | ASTM D-638 | 40 | % | ||
| IZOD冲击强度 | 1/4" | ASTM D-256 | 35 | kg.cm/cm | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 7.5 | ft.lb/in | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 103 | ℃ | |
| 热变形温度 | ASTM D-648 | 87(189) | ℉ | ||
| 燃烧性 | File No. E56070 UL&C-UL | - | 1/16"HB | ||
| 维卡软化点 | ASTM D-1525 | 217 | ℉ | ||
| 热变形温度 | ASTM D-648 | 97(206) | ℃ | ||