| 类型 | 标准料 |
| 密度 | 1.19 |
| 牌号 | 7M |
| 销售方式 | 品牌经销 |
| 颜色 | 本色 |
| 用途级别 | 板材级,型材 |
| 品牌 | 赢创德固赛 |
| 厂家(产地) | 德国 |
| 加工级别 | 挤出级 |
| 特性级别 | 标准级,透明级,高强度,高抗冲 |
| 规格级别 | 透明 |
Plexiglas® 7M 聚甲基丙烯酸甲酯-丙烯酸 Evo
nik Industries AG 产品说明：
Product Profile:
PLEXIGLAS® 7M is based on polymethyl methacrylate (PMMA).
Besides showing the familiar properties of PLEXIGLAS® 7H molding compounds, such as
excellent light transmission and brilliance excellent weatherability high mechanical strength, surface hardness and abrasion resistance.
PLEXIGLAS® 7M is special in that it
better flowing behavior, AMECA listing.
Application:
PLEXIGLAS® 7M is particularly suitable for extruding profiles and panels for use in lighting engineering.
Examples:
lighting fixtures, displays and similar extruded items for technical purposes.
Plexiglas® 7M 物性表
| 基本信息 | |
| 黄卡编号 | E65495-247806 |
| 特性 | 高强度 光稳定 耐气候影响性能良好 硬度高 |
| 用途 | Displays 照明装置 |
| 形式 | 粒子 |
| 加工方法 | 挤出 |
| 多点数据 | Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.19 | g/cm3 | ISO 1183 |
| 溶化体积流率（MVR） (230°C/3.8 kg) | 2.90 | cm3/10min | ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | 3200 | MPa | ISO 527-2/1 |
| 拉伸应力 (断裂) | 69.0 | MPa | ISO 527-2/5 |
| 拉伸应变 (断裂) | 4.0 | % | ISO 527-2/5 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁无缺口冲击强度 (23°C) | 20 | kJ/m2 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 玻璃转化温度 | 108 | °C | ISO 11357-2 |
| 维卡软化温度 | 104 | °C | ISO 306/B50 |
| 线形热膨胀系数 - 流动 (0 到 50°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| 可燃性 | 额定值 | | 测试方法 |
| UL 阻燃等级 (1.60 mm) | HB | | UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
| 折射率 | 1.490 | | ISO 489 |
| 透射率 1 | 92.0 | % | ISO 13468-2 |
| 挤出 | 额定值 | 单位制 | |
| 干燥温度 | < 94.0 | °C | |
| 干燥时间 | 2.0 到 3.0 | hr | |
| 熔体温度 | 220 到 260 | °C | |
| 口模温度 | 220 到 260 | °C |