| 牌号 | HI-835M |
| 用途级别 | 高抗冲型 |
| 产地/厂家 | 韩国LG |
| 品牌 | PMMA |
| 型号 | HI-835M |
| 厂家(产地)：韩国LG | 牌号：HI835M | 用途级别：高抗冲型 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 230℃/3.8kgs | ASTM D-1238 | 1.5 | g/10min |
| 吸水率 | --- | ASTM D-570 | 0.3 | % |
| 物理性能 | 收缩率 | --- | ASTM D-955 | 0.002-0.006 | --- |
| 比重 | --- | ASTM D-792 | 1.19 | --- |
| 总透光率 | --- | ASTM D-1003 | 93 | % |
| 折射率 | --- | ASTM D-542 | 1.49 | --- |
| 机械性能 | 抗拉强度 | --- | ASTM D-638 | 660 | kg/cm2 |
| 拉伸强度 | --- | ASTM D-638 | 5 | % |
| 抗挠强度 | --- | ASTM D-790 | 1100 | kg/cm2 |
| 弯曲弹性率 | --- | ASTM D-790 | 33000 | kg/cm2 |
| IZOD缺口冲击强度 | --- | ASTM D-256 | 1.5 | kg.cm/cm |
| 洛氏硬度 | --- | ASTM D-785 | 94 | M scale |
| 热 性 能 | 热变形温度 | 有退火 | ASTM D-648 | 89 | ℃ |
| 热变形温度 | 无退火 | ASTM D-648 | 80 | ℃ |
| 维卡软化点 | --- | ASTM D-1525 | 99 | ℃ |
| 燃烧性 | --- | UL 94 | HB | CLASS |
| 其它性能 | 贝兹 | --- | ASTM D-1003 | 0.3 | % |
PMMA 韩国LG HI855S
PMMA 韩国LG IF830
PMMA 韩国LG IF850
PMMA 韩国LG IH830
PMMA 韩国LG IH830C
PMMA 韩国LG IG840
PMMA 韩三星 TF-0956
PMMA 德国赢创德固赛 6N
PMMA 德国赢创德固赛 8N
PMMA 德国赢创德固赛 8NDF21
PMMA 德国赢创德固赛 8NDF22
PMMA 德国赢创德固赛 8NDF23
PMMA 德国赢创德固赛 8NDF20
PMMA 德国赢创德固赛 ZK40
PMMA 德国赢创德固赛 ZK5BR
PMMA 泰国三菱 IRG-404
PMMA 日本三菱丽阳 MF001
PMMA 日本三菱丽阳 VH5
PMMA 日本三菱丽阳 VRF60-001ML
PMMA 日本三菱丽阳 640
PMMA 日本三菱丽阳 IRD-30
PMMA 日本三菱丽阳 IRD-70
PMMA 日本三菱丽阳 IRK-304
PMMA 日本三菱丽阳 MD001
PMMA 日本三菱丽阳 SV001
PMMA 日本三菱丽阳 IRS-404
PMMA 日本三菱丽阳 MF-NW432
PMMA 日本三菱丽阳 TF8-000
PMMA 日本三菱丽阳 VH-067A
PMMA 日本三菱丽阳 VRL-40
PMMA 日本三菱丽阳 VRM-40
PMMA 日本三菱丽阳 TF8
PMMA 日本三菱丽阳 VKL40F
PMMA 日本三菱丽阳 IRD-50
PMMA 日本三菱工程 VH
PMMA 日本三菱丽阳 VH001
PMMA 日本三菱 VHPF-083 BK
021-80107851