| 厂家(产地) | 台湾化纤 |
|---|---|
| 牌号 | 3224 |
| 加工级别 | 挤出级,吹塑级 |
| 用途级别 | 薄膜级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.920 | g/cm3; | |
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 2.0 | g/10 min | |
薄膜 | 薄膜厚度 | 经测试 | 38 | μm | |
| 割线模量 | 1% 正割, MD: 38 μm, 吹塑薄膜 | ASTM D882 | 147 | MPa | |
| 1% 正割, TD: 38 μm, 吹塑薄膜 | ASTM D882 | 206 | MPa | ||
| 抗张强度 | MD: 屈服, 38 μm, 吹塑薄膜 | ASTM D882 | 9.81 | MPa | |
| TD: 屈服, 38 μm, 吹塑薄膜 | ASTM D882 | 10.8 | MPa | ||
| MD: 断裂, 38 μm, 吹塑薄膜 | ASTM D882 | 35.3 | MPa | ||
| TD: 断裂, 38 μm, 吹塑薄膜 | ASTM D882 | 27.5 | MPa | ||
| 伸长率 | MD: 断裂, 38 μm, 吹塑薄膜 | ASTM D882 | 600 | % | |
| TD: 断裂, 38 μm, 吹塑薄膜 | ASTM D882 | 800 | % | ||
| 落锤冲击 | 38 μm, 吹塑薄膜 | ASTM D1709 | 120 | g | |
| 埃尔曼多夫抗撕强度 | MD: 38 μm, 吹塑薄膜 | ASTM D1922 | 61 | g | |
| TD: 38 μm, 吹塑薄膜 | ASTM D1922 | 650 | g | ||
| 热性能 | 脆化温度 | ASTM D746 | -70.0 | °C | |
| 维卡软化温度 | ASTM D1525 | 93.0 | °C | ||
| 熔融温度 | ASTM D1525 | 122 | °C | ||