| 厂家(产地) | 韩国锦湖 |
|---|---|
| 牌号 | GP-125 |
| 加工级别 | 注塑级 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃,5kg | ASTM D-1238 | 2.5 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.030 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 模具收缩率 | ASTM D-955 | 0.30-0.60 | % | ||
| 机械性能 | 屈服拉伸强度 | ASTM D-638 | 53.8 | MPa | |
| 屈服伸长率 | ASTM D-638 | 2.0 | % | ||
| 弯曲模量 | ASTM D-790 | 3130 | MPa | ||
| 屈服弯曲强度 | ASTM D-790 | 97.9 | MPa | ||
| IZOD缺口冲击强度 | 3.18mm | ASTM D-256 | 21.9 | J/m | |
| 洛氏硬度 | ASTM D-785 | 80 | M scale | ||
| 电气性能 | 体积电阻率 | ASTM D-257 | 1.0×1016 | ohm.cm | |
| 介电强度 | ASTM D-149 | 21.7 | KV/mm | ||
| 介电常数 | 1×106Hz | ASTM D-150 | 2.500 | ||
| 热性能 | 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 92.2 | ℃ |
| 维卡软化点 | ASTM D-1525 | 107 | ℃ | ||
| 燃烧性 | 1.59mm | HB | UL 94 | ||
| 燃烧性 | 3.18mm | UL 94 | HB | ||
| 燃烧性 | 6.35mm | UL 94 | HB | ||
| RTI Str | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Str | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Str | 6.35mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 6.35mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 6.35mm | UL 746 | 50.0 | ℃ | |
021-80107851