| 厂家(产地) | 韩国锦湖 |
| 牌号 | HW603E |
| 加工级别 | 挤出级 |
| 特性级别 | 耐低温,高抗冲 |
| 销售方式 | 品牌经销 |
| 类型 | 标准料 |
苏州煜昇塑化有限公司
HW603E is an extrusion grade AES resin, offering excellent weather resistance and excellent low temperature impact strength.
HW603E is recommended for park tables,skiing boards,road signals and automobile parts, etc. |
| 材料状态 | 已商用：当前有效 |
| 资料 1 | Technical Datasheet (English) |
| 搜索 UL 黄卡 | Shanghai KumhoSunny Plastics Co., Ltd. |
| 供货地区 | 亚太地区 |
| 性能特点 | |
| 用途 | 室外应用 |
| 加工方法 | |
| 比重 2 | 1.04 | g/cm³ | ASTM D792 |
| 熔流率 (220°C/10.0 kg) | 12 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (23°C) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度 (R 计秤, 23°C) | 102 | | ASTM D785 |
| 抗张强度 3 (断裂) | 50.0 | MPa | ASTM D638 |
| 伸长率 3 (断裂) | 45 | % | ASTM D638 |
| 弯曲模量 4 | 2200 | MPa | ASTM D790 |
| 弯曲强度 4 | 68.0 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C, 3.18 mm) | 350 | J/m | ASTM D256 |
| 热变形温度 (1.8 MPa, 未退火) | 85.0 | °C | ASTM D648 |
| 维卡软化温度 | 95.0 | °C | ASTM D1525 5 |
| 表面电阻率 | > 1.0E+14 | ohm | IEC 60093 |
| 体积电阻率 | > 1.0E+14 | ohm·cm | IEC 60093 |
| UL 阻燃等级 (1.59 mm) | HB | | UL 94 |
| 干燥温度 | 80.0 到 90.0 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议注入量 | 40 到 70 | % | |
| 螺筒后部温度 | 190 到 210 | °C | |
| 螺筒中部温度 | 200 到 230 | °C | |
| 螺筒前部温度 | 200 到 220 | °C | |
| 射嘴温度 | 200 到 220 | °C | |
| 加工（熔体）温度 | 200 到 230 | °C | |
| 模具温度 | 50.0 到 80.0 | °C | |
| 背压 | 1.00 到 5.00 | MPa | |
| 螺杆转速 | 30 到 60 | rpm | |
AES树脂（丙烯腈-EPDM橡胶-苯乙烯共聚物）具有**的耐候性，即使长时间暴露在室外紫外线、潮湿、雨淋、光照及臭氧条件下，不经涂装也可以保持物性稳定。特别适合不涂装在户外直接使用。 ??AES塑胶原料概述与定义：工程塑料的定义**是可以代替金属制品的塑胶原料，它的耐温至少到达100度**高可以达到1000度，它本色重量很轻，有良好的刚性，通过改性可以达到很多种物理特性，一般的塑胶原料的来源都是以石油而提炼出来的化学品。是经过聚合反应得到的高分子树脂。加强工程塑料防火的添加剂有：卤素及非卤素（磷酸脂）防火剂。化学性能增强 ：安定剂、抗氧化剂、表面处理改质剂。物理性能增强可添加：：玻璃纤维、碳纤维、矿物质等