| 类型 | 标准料 |
|---|---|
| 牌号 | 2050 |
| 销售方式 | 品牌经销 |
| 用途级别 | 薄膜级 |
| 厂家(产地) | 韩国韩华 |
| 加工级别 | 注塑级 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.934 | g/cc | ||
| 熔体流动速率 | ASTM D-1238 | 1.0 | g/10min | |||
| 机械性能 | 拉伸断裂强度 | ASTM D-638 | 200 | kg/cm2 | ||
| 断裂伸长率 | ASTM D-638 | 780 | % | |||
| 断裂伸长率 | MD | ASTM D-882 | 370 | % | ||
| TD | ASTM D-882 | 680 | % | |||
| 拉伸断裂强度 | MD | ASTM D-882 | 285 | kg/cm2 | ||
| TD | ASTM D-882 | 270 | kg/cm2 | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 72 | ℃ | ||
| 熔点 | ASTM D-2117 | 96 | ℃ | |||
| 其它性能 | 厚度 | HCC Method | 0.06 | mm | ||
| 醋酸乙烯含量 | HCC Method | 12.0 | Wt% | |||
| 拉伸抗热强度 | MD | ASTM D-1004 | 75 | kg/cm | ||
| TD | ASTM D-1004 | 80 | kg/cm | |||
| 下降冲击强度 | ASTM D-1709 | ＞400 | g | |||
| 混浊度 | ASTM D-1009 | 1.5 | % | |||