产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 200℃,5kg | ASTM D-1238 | 0.9 | g/10min |
| 比重 | 23℃ | ASTM D-792 | 1.077 | ||
| 机械性能 | 引张强度 | 1/8",6mm/min | ASTM D-638 | 786(11150) | kg/cm2(lb/in2) |
| 延伸率 | 1/8",6mm/min | ASTM D-638 | 7 | % | |
| 弯曲强度 | 1/4",2.8mm/min | ASTM D-790 | 1244(17643) | kg/cm2(lb/in2) | |
| 弯曲弹性率 | 1/4",2.8mm/min | ASTM D-790 | 35280(49754) | kg/cm2(lb/in2) | |
| IZOD缺口冲击强度 | 1/4",23℃ | ASTM D-256 | 2.1(0.39) | kg.cm/cm(fg-lb/in) | |
| IZOD缺口冲击强度 | 1/8",23℃ | ASTM D-256 | 2.5(0.48) | kg.cm/cm(fg-lb/in) | |
| 硬度 | 1/4" | ASTM D-785 | 85 | M Scale | |
| 热性能 | 软化点 | 1/8",50℃/hr | ASTM D-1525 | 103.5(218) | ℃(℉) |
| 热变形温度 | 1/4",120℃/hr,退火 | ASTM D-648 | 99.5(211)) | ℃(℉) | |
| 热变形温度 | 1/4",120℃/hr,未退火 | ASTM D-648 | 90.5(195) | ℃(℉) | |