性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | 200℃,5kg | ASTM D-1238(ISO 1133) | 5.5 | g/10min |
熔体流动速率 | 200℃,10kg | ASTM D-1238(ISO 1133) | 35 | g/10min | |
吸水率 | ASTM D-570 | 0.3 | % | ||
物理性能 | 模塑收缩率 | ASTM D-75 | 0.4-0.7 | % | |
比重 | ASTM D-792 | 1.04 | |||
机械性能 | 拉伸强度 | 23℃ | ASTM D-638 | 480 | Kg/cm2 |
断裂伸长率 | ASTM D-638 | 15 | % | ||
弯曲强度 | 23℃ | ASTM D-790 | 670 | Kg/cm2 | |
弯曲模量 | 23℃ | ASTM D-790 | 24000 | Kg/cm2 | |
IZOD缺口冲击强度 | 6.4mm | ASTM D-256 | 22 | kg.cm/cm | |
洛氏硬度 | ASTM D-785 | 110 | R scale | ||
热性能 | 热变形温度 | 6.4mm,18.6kg/cm2未退火 | ASTM D-648 | 85 | ℃ |
阻燃性 | UL-94 | HB | class |