产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.7 | % |
吸水率 | 饱和(23℃) | ASTM D-570 | 5.4 | % | |
物理性能 | 比重 | ASTM D-792 | 1.38 | ||
机械性能 | 洛氏硬度M | DAM | ASTM D-785 | M101 | |
拉伸强度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa | |
埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | j/m | |
埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 107 | j/m | |
断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % | |
挠曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa | |
挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | MPa | |
挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | ||
挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | MPa | |
拉伸强度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa | |
泰伯磨耗量 | 50%RH | 14 | cycles | ||
断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
电气性能 | 介电强度 | DAM | ASTM D-149 | 530 | volts/mil |
介电强度 | (分步法) | ASTM D-149 | 440 | volts/mil | |
体积电阻率 | 100%RH | ASTM D-257 | 109 | ohm-cm | |
体积电阻率 | DAM | ASTM D-257 | 1015 | ohm-cm | |
介电常数 | DAM@103Hz赫 | ASTM D-150 | 4.5 | ||
介电常数 | 100%RH@106Hz赫 | ASTM D-150 | 10.7 | ||
损耗因数 | DAM@103Hz赫 | ASTM D-150 | 0.02 | ||
介电常数 | 100%RH@103Hz赫 | ASTM D-150 | 25.0 | ||
损耗因数 | 100%RH@106Hz赫 | ASTM D-150 | 0.02 | ||
介电常数 | DAM@106Hz赫 | ASTM D-150 | 3.7 | ||
热性能 | 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ |
线性热膨胀系数 | ASTM D-696 | 2.3×10-5 | m/m/℃ | ||
熔点 | DAM | ASTM D-789 | 255 | ℃ | |
熔点 | 50%RH | ASTM D-789 | 255 | ℃ |
PA66(聚酰胺66或尼龙66),同PA6相比,PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。
聚酰胺树脂,英文名称为polyamide,简称PA。俗称尼龙(Nylon),它是大分子主链重复单元中含有酰胺基团的高聚物的总称。为五大工程塑料中产量最大、品种最多、用途最广的品种。尼龙中的主要品种是尼龙6和尼龙66,占绝对主导地位,尼龙6为聚己内酰胺,而尼龙66为聚己二酸己二胺,尼龙66比尼龙6要硬l2%;其次是尼龙11,尼龙12,尼龙610,尼龙612,另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13,新品种有尼龙6I、尼龙9T和特殊尼龙MXD6(阻隔性树脂)等,尼龙的改性品种数量繁多,如增强尼龙、单体浇铸尼龙(MC尼龙)、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲(超韧)尼龙、电镀尼龙、导电尼龙、阻燃尼龙,尼龙与其他聚合物共混物和合金等,满足不同特殊要求,广泛用作金属,木材等传统材料代用品。