| 厂家 | 赢创德固赛 |
| 类型 | 标准料 |
| 名称 | PA12 |
| 牌号 | L1670 |
| 销售方式 | 品牌经销 |
| 用途级别 | 注塑级,照明灯具,汽车部件,高性能级,高流动性级,电子电器部件 |
| 品牌 | PA12 德国赢创德固赛 L1670 |
| 加工级别 | 注塑级 |
| 特性级别 | 标准级,增韧级,增强级 |
| 规格级别 | 注塑 |
VESTAMID? L L1670 聚酰胺12 Evo
nik Industries AG 产品说明： Unfilled polyamid 12 compounds
Characterization: low viscosity, heat and light stabilized, with processing aid
Application Examples: wire insulation, coils, seco
ndary coating of optical fibers
The properties of PA 12 compounds can be modified to suit the requirements of many applications by incorporating various additives such as stabilizers, plasticizers, reinforcements, and fillers.
The VESTAMID? L compounds of Evo
nik comprise a range of various products that are customized to the requirements of processors and users. Many of the PA 12 compounds are suitable especially for the injection molding of recision parts; others have been developed specifically for the extrusion process. VESTAMID? L L1670 物性表
| 基本信息 | |
| 添加剂 | 加工助剂 热稳定剂 紫外线稳定剂 |
| 特性 | 低粘度 高 ESCR（抗应力开裂） 光稳定 减震 降噪 抗溶剂性 抗撞击性，良好 可加工性，良好 良好耐磨损性 耐疲劳性能 耐燃油性 耐油性能 耐油脂性能 热稳定性 吸水低或不吸水 |
| 用途 | 电线电缆应用 绝缘材料 涂层应用 |
| 机构评级 | 欧洲 10/1/2011 12:00:00 AM |
| 加工方法 | 挤出 注射成型 |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 (23°C) | 1.01 | g/cm3 | ISO 1183 |
| 收缩率 | | | ISO 294-4 |
| 垂直流动方向 | 1.1 | % | ISO 294-4 |
| 流动方向 | 0.90 | % | ISO 294-4 |
| 吸水率 | | | ISO 62 |
| 饱和, 23°C | 1.4 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.70 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | 1400 | MPa | ISO 527-2 |
| 拉伸应力 (屈服) | 46.0 | MPa | ISO 527-2 |
| 拉伸应变 | | | ISO 527-2 |
| 屈服 | 6.0 | % | ISO 527-2 |
| 断裂 | > 50 | % | ISO 527-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | | | ISO 179/1eA |
| -30°C, 完全断裂 | 5.0 | kJ/m2 | ISO 179/1eA |
| 23°C, 完全断裂 | 4.0 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度 | | | ISO 179/1eU |
| -30°C | 无断裂 | | ISO 179/1eU |
| 23°C | 无断裂 | | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 热变形温度 | | | |
| 0.45 MPa, 未退火 | 120 | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 50.0 | °C | ISO 75-2/A |
| 维卡软化温度 | | | |
| -- | 170 | °C | ISO 306/A |
| -- | 140 | °C | ISO 306/B |
| 熔融温度 1 | 178 | °C | ISO 11357-3 |
| 线形热膨胀系数 - 流动 (23 到 55°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 体积电阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度 | 27 | kV/mm | IEC 60243-1 |
| 相对电容率 | | | IEC 60250 |
| 23°C, 100 Hz | 3.80 | | IEC 60250 |
| 23°C, 1 MHz | 2.20 | | IEC 60250 |
| 耗散因数 | | | IEC 60250 |
| 23°C, 100 Hz | 0.045 | | IEC 60250 |
| 23°C, 1 MHz | 0.028 | | IEC 60250 |
| 漏电起痕指数 | | | IEC 60112 |
| -- | 600 | V | IEC 60112 |
| 解决方案 A 2 | > 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | | | UL 94 |
| 1.60 mm | HB | | UL 94 |
| 3.20 mm | HB | | UL 94 |
| 补充信息 | 额定值 | | 测试方法 |
| Electrolytical Corrosion | A1 | | IEC 60426 |
| ISO Shortname | PA12, KHL, 12-010 | | ISO 1874 |
| 备注 |
| 1 . | 2nd Heating |
| 2 . | 50 drops value |